Active Brazing Alloys

Active Brazing Alloys eliminate the need for traditional ceramic metallization prior to brazing as the active components promotes wetting on the ceramic surface.

active brazing alloy materials

One-step brazing with ABA® replaces metallizing, firing and electroplating, offering savings in time and cost. ABA®’s are available in Gold, Silver, Titanium and Copper based materials and offer highly reliable hermetic seal between ceramic and metal for both oxide and non-oxide ceramics. Available alloy forms include foil, preforms, wire and paste.

alloy forms

Also view: Materials - Active Brazing Alloys

Active Brazing Alloys - Properties

Name	Nominal Composition Percent	Liquidus		Solidus		Form Availability
Name	Nominal Composition Percent	°C	°F	°C	°F	Form Availability
Gold-ABA®-V	Au – 97.5 Ni – 0.75 V – 1.75	1090	1994	1045	1913	Wire, Foil
Gold-ABA®	Au – 96.4 Ni – 3 Ti – 0.6	1030	1886	1003	1837	Wire, Foil
Copper-ABA® (L)	Cu – 92.75 Si – 3.0 Al – 2.0 Ti – 2.25	1024	1875	958	1756	Wire, Foil
Nioro® - ABA™	Au – 82.0 Ni – 15.5 V – 1.75 Mo – 0.75	960	1760	940	1725	Wire, Foil
Tini-67™	Ti – 67.0 Ni – 33.0	980	1795	942	1730	Foil, Paste
Ticuni®	Ti – 70 Ni – 15 Cu – 15	960	1760	910	1670	Foil, Paste
Ticuni-60®	Ti – 60 Ni – 25 Cu – 15	940	1725	890	1630	Foil, Paste
Silver-ABA®	Ag – 92.75 Cu – 5.0 Al – 1.0 Ti – 1.25	912	1673	860	1580	Wire, Foil, Paste
Ticusil®	Ag – 68.8 Cu – 26.7 Ti – 4.5	900	1650	780	1435	Wire, Foil, Paste
Cusil-ABA®	Ag – 63.0 Cu – 35.25 Ti – 1.75	815	1500	780	1435	Wire, Foil, Paste
Cusin-1-ABA®	Ag – 63.0 Cu – 34.25 Sn – 1.0 Ti – 1.75	805	1483	775	1427	Wire, Foil, Paste
Incusil®-ABA™	Ag – 59.0 Cu – 27.25 In – 12.5 Ti – 1.25	715	1319	605	1121	Wire, Foil, Paste
Impurity Limits – All other metallic impurities having a vapor pressure higher than 10-7 mm Hg at 500°C are limited to .002% each. Impurities having a vapor pressure lower than 10-7 mm Hg at 500°C are limited to a total of .050%. (Applicable to all forms except powder and extrudable paste).